BES-Exposed Aggregate Materials
This product contains gel, gas guide, water reducer, Aomi fiber and other polymer, special polymer materials, and cement and other organomineral admixture composition of cementing material, through the corresponding graded
aggregate site mixing construction. Its terminal products are high water permeability, skid resistance, ground temperature regulation and easy cleaning; high impact and high stripping are better than ordinary concrete.
Surface Layer: 15kg/m³
Bottom Layer: 10kg/m³
How to use: Mix with concrete until even
Polystyrene polymer emulsion mainly plays the role of interface bonding and ensuring the uniform permeability of the gap, which can make the connection between the stones more firm, and improve the permeability effect.
Standard dosage: 3 kg/m³
How to use:Mix with concrete until even.
This product is a polyurethane sealant for drying exposed aggregate permeable concrete. Excellent permeability, deep penetration substrate to 3-5mm, containing alkali surface water replacement, in order to achieve the touch and eliminate color difference, at the same time, the product reaction will form a layer of tough transparent high gloss film, greatly improve the road wear resistance and reduce the occurrence of aggregate loss phenomenon in use, provide lasting protection to the road surface, bright as new. After curing, the product is a completely transparent and tough chemical product. The product is an aliphatic polyurethane curing product, with no yellowing.
Erosion inhibitor is used to slow the coagulation of the surface mortar of the natural stone, and make the surface layer mortar slow coagulation under the premise that the foundation is solidified firmly.Within two hours of the completion of the permeable concrete pavement, the retarder is sprayed to the surface of the permeable concrete, and then cover the film for maintenance. After about 10 hours, wash the mortar on the surface with water, and then cover the film until the strength of the permeable concrete comes up.